All-solid-state lithium-ion batteries (LIBs) are one of the promising candidates to overcome some issues of conventional LIBs with liquid electrolytes. However, high interfacial resistance of Li-ion transfer at the electrode/solid electrolyte limits their performance. Thus, it is important to clarify interfacial phenomena in a nanometer scale. Here, we present a new method to dynamically observe the Li-ion distribution and Co-ion electronic states in a LiCoO 2 cathode of the all-solid-state LIB during charge and discharge reactions using operando scanning transmission electron microscopy (STEM) and electron energy-loss spectroscopy (EELS). By applying a hyperspectral image analysis of non-negative matrix factorization (NMF) to the STEM-EELS, we succeeded in clearly observing the quantitative Li-ion distribution in the operando condition. We found from the operando observation with NMF that the Li ions did not uniformly extract/insert during the charge/discharge reactions, and the activity of the electrochemical reaction depended on the Li-ion concentration in a pristine state. An electrochemically inactive region was formed about 10–20 nm near the LiCoO 2 /Li 2 O–Al 2 O 3 –TiO 2 –P 2 O 5 -based solid electrolyte interfaces. The STEM-EELS, electron diffraction, and Raman spectroscopy experimentally showed that the inactive region was a mixture of LiCoO 2 and Co 3 O 4, leading to the higher interfacial resistance of the Li-ion transfer because Co 3 O 4 does not have pathways of Li-ion diffusion in its crystal.
No takes yet. Share an insight, caveat, or question.
Nomura et al. (2018) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: