MgNiO-based metal–semiconductor– metal ultraviolet photodetector

In this study, we report the growth of Mg x Ni 1− x O thin films on quartz substrates by electron beam evaporation. The absorption edge shows a blue shift from 340 nm to 260 nm with increase in the Mg content from 0.2 to 0.8. A metal–semiconductor–metal structured photodetector is fabricated from the Mg 0.2 Ni 0.8 O film. At a bias of 5 V, the dark current of the photodetector is about 70 nA. The maximum responsivity is about 147.3 µA W −1 at 320 nm. In addition, the ultraviolet (UV) (320 nm) to visible (400 nm) rejection ratio is nearly two orders of magnitude. Based on these results, it is proposed that Mg x Ni 1− x O is a potential candidate for application in UV photodetectors.