In present work, an investigation was carried out about the various important properties of Yb 3+ substituted Potassium based ?-hexaferrite KFe 11-x Yb x O 17 (x= 0.0, 0.02, 0.06, 0.1). The Sol-gel auto combustion technique was used to synthesize all the samples. The X-ray diffraction (XRD) patterns confirmed the single hexagonal phase for all prepared samples. The Scanning Electron Microscopy (SEM) confirmed the agglomeration of small particles into big grains. The DC electrical resistivity, measured in the voltage range of (-200V) to (200V), was observed to vary with Yb 3+ contents. The Polarization versus electric field loops revealed the lossy behaviour of pure and substitute samples which indicated the resistive nature of the samples. The saturation and remanence polarization first decreased and then increased with Yb 3+ substitution due to ferric ions distribution between octahedral sites and resistive nature of the samples, respectively. The samples exhibited peculiar magnetic behaviour with the substitution of Yb 3+ ions. The saturation magnetization was increased up to concentration x = 0.06 and then decreased with further substitution of Yb 3+ contents. The coercivity values varied in the range of 141.43 to 279.26 Oe for all the samples which confirmed the soft magnetic nature of present synthesized material. The real part (µ’) and imaginary part (µ’’) of permeability exhibited the high values at low frequencies and these values decreased with the increase of frequency. The prepared samples were supposed to be used as core material of transformer and in high frequency applications due to high resistivity value and low eddy current losses.
No takes yet. Share an insight, caveat, or question.
Raheel et al. (2022) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: