The present study intended to find a way to use TiO₂, one of the most widely used photocatalysts, as a construction material. To that end, nano-SiO₂/Al₂O₃-TiO₂ powder (NTCP) was synthesized by coating SiO₂ and Al₂O₃ support materials with TiO₂. The NTCP was anatase phase spherical particles, specific surface areas were 319 m²/g and 267 m²/g for the SiO₂-TiO₂ powder and Al₂O₃-TiO₂ powder. UV absorption test results showed the developed NTCP had a light absorption peak at wavelengths of 380 nm or below, and its absorbance was much larger than that of commercial TiO₂. The NTCP formed smaller pores on the surface than commercial TiO₂. As a result, the flow of the mortar decreased as the adsorption strength increased and combined a large number of water molecules. In addition, the Pozzolanic reaction by SiO₂ and Al₂O₃ used as support materials produced many calcium silicate hydrate (C-S-H) and calcium aluminate hydrate (C-A-H). This has shown an increased strength of mortar mixed with the NTCP by promoting a nucleation effect and reducing the filling effect and the number of harmful holes in the mortar.
No takes yet. Share an insight, caveat, or question.
Lee et al. (2019) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: