NBTI Degradation in LTPS TFTs Under Mechanical Tensile Strain

This letter investigates the negative-bias temperature instability (NBTI) degradation of p-channel low-temperature polycrystalline-silicon thin-film transistors (LTPS TFTs) under mechanical tensile stress. Experimental results reveal that the interface state densityNitand grain boundary trap densityNtrapof tensile-strained LTPS TFTs are more pronounced than those of unstrained LTPS TFTs. Extracted density of states and conduction activation energyEaboth show increases due to the strained Si-Si bonds, which implies that strained Si-Si bonds are able to react with dissociated H during NBTI stress. Therefore, NBTI degradation is more significant after tensile strain than in an unstrained condition.