Healable network polymers bearing flexible poly(lauryl methacrylate) chains via thermo‐reversible furan‐maleimide diels–alder reaction

A new ATRP initiator containing two furyl rings, namely, bis(furan‐2‐ylmethyl) 2‐bromopentanedioate was synthesized starting from commercially available l ‐glutamic acid as a precursor. Well‐defined bisfuryl‐terminated poly(lauryl methacrylate) macromonomers with molecular weight and dispersity in the range 5000–12,000 g mol −1 and 1.30–1.37, respectively, were synthesized employing the initiator by atom transfer radical polymerization (ATRP). Independently, 1,1′,1″‐(nitrilotris(ethane‐2,1‐diyl))tris(1H‐pyrrole‐2,5‐dione) was synthesized as a tris‐maleimide counterpart for furan‐maleimide click reaction. Thermo‐reversible network polymer bearing flexible poly(lauryl methacrylate; (PLMA) chains was obtained by furan‐maleimide Diels–Alder click reaction of bisfuryl‐terminated PLMA with 1,1′,1″‐(nitrilotris(ethane‐2,1‐diyl))tris(1H‐pyrrole‐2,5‐dione). The prepared network polymer showed retro‐Diels–Alder reaction in the temperature range 110–170 °C as determined from DSC analysis. The presence of low Tg (–40 °C) PLMA chains induced chain mobility to the network structure which led to the complete scratch healing of the coating at 60 °C in five days due to furan‐maleimide adduct formation. The storage modulus of the network polymer was found to be 3.7 × 10 4 Pa at the constant angular frequency of 5 rad/sec and strain of 0.5%. The regular reversal of storage ( G ′) and loss modulus ( G ″) was observed with repeated heating (40 to 110 °C) and cooling cycles (110 to 40 °C) at constant angular frequency and strain.