Ni‐based superalloys with niobium (Nb) or/and yttrium (Y) were prepared by vacuum melting. The oxidation kinetics of these alloys was studied by thermogravimetry at 800 °C for 100 h in static air. Morphology of oxides was studied using SEM, and the composition was analyzed by X‐ray diffraction. Energy‐dispersive X‐ray spectrometer was employed to examine the linear element distribution of the cross section of the oxidation films. Results showed that the oxidation kinetics all followed a parabolic law at different stages. The oxide films were mainly comprised of Cr 2 O 3 , NiCr 2 O 4 , Al 2 O 3 and TiO 2 . All the oxide films exhibited layered structure owing to different oxidation stages. With the addition of Nb or Y, the high‐temperature oxidation resistance of the superalloy was improved significantly and the surface morphology of the oxidation film was ameliorated. The comprehensive effect of Nb and Y was remarkable in improving the high‐temperature oxidation resistance of Ni‐based alloys.
No takes yet. Share an insight, caveat, or question.
Weng et al. (2014) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: