Preparation and Properties of Surface-Coated HMX with Viton and Graphene Oxide

To improve the safety performance of HMX (octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine) particles, the new carbon material graphene oxide (GO) and Viton were used to coat HMX via a solvent–slurry process. For comparison, the HMX/Viton/graphite (HMX/Viton/G) and HMX/Viton composites were also prepared by the same process. Atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and differential scanning calorimetry (DSC) were employed to characterize the morphology, composition, and thermal decomposition of samples. The impact sensitivity and shock wave sensitivity of HMX-based composites were also measured and analyzed. The results of SEM, XRD, and XPS indicate that the cladding layer of HMX-based composites is successfully constructed. HMX/Viton/GO composites exhibit better thermal stability compared to HMX and HMX/Viton. The results show that both impact and shock wave sensitivities of HMX/Viton/GO composites are much lower than that of HMX/Viton. In addition, GO sheets exhibit a better desensitizing effect than G sheets. These combined properties suggest that nano-GO has good compatibility with explosives and can be utilized as a desensitizer in HMX particles.