Studies on sulfonic acid functionalized hollow silica spheres/Nafion® composite proton exchange membranes

In this work, sulfonic acid functionalized hollow silica spheres (SAFHSS)/Nafion® composite membranes were prepared by a recasting procedure. The influences of temperature on water uptake, swelling degree, and proton conductivity of the composite membranes were studied. In comparison with the pure recast Nafion® membrane, it was found that water uptake of composite membranes increased with increasing SAFHSS loading at all temperature studied. The swelling degree of SAFHSS/Nafion® composite membranes with 10∼15 wt % SAFHSS loading was lower than that of the pure recast Nafion® at all temperatures in the study. The proton conductivity of SAFHSS/Nafion® composite membranes was constantly higher than that of the pure recast Nafion® at all temperatures (50∼130 °C). In a range from 50 to 130 °C, the highest conductivity of composite membranes was obtained when 10 wt % SAFHSS was loaded. The maximum conductivity reached 0.1 S cm −1 at 100% relative humidity and 100 °C, even the temperature reached to 130 °C, the conductivity of the composite membranes with 10 wt % SAFHSS was still as high as 4.4 × 10 −2 S cm −1 at 100% relative humidity, whereas the conductivity of the pure recast Nafion® was only 2.2 × 10 −3 S cm −1 .