Effect of nitrogen doping on TiOxNy thin film formation at reactive high-power pulsed magnetron sputtering

This is the authors' abstract. We don't add key points for this paper.

The paper is focused on a study of formation of TiO x N y thin films prepared by pulsed magnetron sputtering of metallic Ti target. Oxygen and nitrogen were delivered into the discharge in the form of reactive gases O 2 and N 2 . The films were deposited by high-power impulse magnetron sputtering working with discharge repetition frequency f = 250 Hz at low ( p = 0.75 Pa) and high ( p = 10 Pa) pressure. The substrates were on floating potential and thermally stabilized at room temperature during the deposition process. Post-deposition thermal annealing was not employed. The chemical composition from x-ray photoelectron spectroscopy diagnostic reveals formation of TiO x N y structure at low flow rate of oxygen in the discharge gas mixture. This result is confirmed by XRD investigation of N element's incorporation into the Ti–O lattice. Decrease in band-gap to values E g ∼ 1.6 eV in TiO x N y thin film is attributed to formed Ti–N bonds. The discharge properties were investigated by time-resolved optical emission spectroscopy. Time evolution of particular spectral lines (Ar + , Ti + , Ti) is presented together with peak discharge current.