We have studied the (001) surface of single crystal YBa2Cu3O7-x high-Tc superconductors using scanning tunnelling microscopy (STM) and atomic force microscopy (AFM) at room temperature at ambient pressure. Both methods show flat terraces with steps which are multiples of the c-axis lattice constant (of 1·17 nm) high. Our results show that the bulk crystal structure extends to the surface and that the crystals were formed by island growth. Only occasionally tunnelling was possible with sample bias voltages below +1·0 V. We interpret the observed voltage dependence and the difficulty to get good STM images to be due to the presence of a less-conducting surface layer. Auger spectroscopy indicates that carbon is present at the surface, which is probably related to a contamination layer.