The controlled synthesis of large-area, atomically thin molybdenum and tungsten ditelluride (MoTe 2 and WTe 2 ) crystals is crucial for their emerging applications based on the attractive electronic properties. However, the solution phase synthesis of high-quality and large-area MoTe 2 or WTe 2 ultrathin films have not been achieved yet. In this study, we synthesized for the first time, large-area atomically thin MoTe 2 and WTe 2 films in solution phase, through rapid crystal formation directly on a conducting substrate. For the synthesis, we developed a new Te precursor. The crystal growth involves an in situ chemical transformation from Te nanoparticles into MoTe 2 or WTe 2 thin films. The synthesis enables precise control of the number of atomic layers over a large area, from a monolayer to multilayers. Micropatterned MoTe 2 thin films are also readily synthesized in situ using the same process. The photodetector made of 3-layer semiconducting MoTe 2 thin films exhibits high photoresponsivity ( R λ ) over a broad spectral range (300–1100 nm) with a maximum in the near-IR region, including a R λ = 30 mA W –1 even at λ = 1.10 μm and a fast photoresponse (87 μs). Our synthesis method presents a crucial step in the solution phase synthesis of metal telluride ultrathin films and paves the way for their large-scale emerging applications.
No takes yet. Share an insight, caveat, or question.
Giri et al. (2018) studied this question.