A small- and wide-angle X-ray scattering study was performed on two metallocene catalyzed isotactic polypropylene (miPP) resins. The results were compared with two similar molecular weight Ziegler–Natta catalyzed isotactic polypropylene (zniPP) materials. Wide-angle X-ray diffraction (WAXD) results showed the existence of two crystalline structures in the metallocene samples, the α-monoclinic and γ-orthorhombic crystal structure, with increasing relative amounts of γ-orthorhombic phase as the lamellae thickness increased. Differential scanning calorimetry (DSC) scans exhibited a melting peak for each crystal structure. The metallocene resins had the same equilibrium melting temperature (186 ± 2 °C) as the high tacticity Ziegler–Natta (ZNHT) resin, whereas a second Ziegler–Natta resin had a lower equilibrium melting temperature (178 ± 2 °C). The equilibrium melting temperature for the γ-orthorhombic crystal structure in the metallocene resins was found to be 178 ± 4 °C. The results were explained by the distribution of defects within the miPP chains, generating higher fold surface free energies for the miPP resins.
No takes yet. Share an insight, caveat, or question.
Bond et al. (1999) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: