In this study, microstructure and corrosion behaviour of homogenized Mg-4Zn-1La magnesium alloy was investigated. Mg-4Zn-1La alloy was produced by low-pressure die casting method. Homogenization treatments were performed at 350 °C and 400 °C for 12, 18, 24 and 48 hours, followed by rapid cooling in water at room temperature. Microstructure characterizations showed that La addition led to a formation of semi-continuous network structure and islands of second phases which identified as T-phase (Mg 7 Zn 3 RE). A significant amount of second phase dissolution and an increase in a-Mg grain size with increasing both homogenization time and temperature was observed. Homogenization treatment led to an improvement in corrosion resistance of Mg-4Zn-1La alloy. Homogenization at 400 °C resulted in better corrosion resistance than homogenization at 350 °C for all homogenization duration.