Ytterbium-doped Sr/sub 5/(PO/sub 4/)/sub 3/F (S-FAP) has been shown to be a useful material for diode pumping, since it displays high gain, low loss, and a long radiative lifetime. One of the issues with S-FAP is that it has a relatively narrow absorption bandwidth (/spl sim/5 nm) at 900 nm, the diode-pumping wavelength, while the diode's output bandwidth can be large (/spl sim/10 nm). By changing the host slightly, the absorption feature can be broadened to better match the pump bandwidth. Four mixed crystal boules of Yb/sup 3+/:Sr/sub 5-x/Ba/sub x/(PO/sub 4/)/sub 3/F were grown by the Czochralski method with x=0.25: 0.5, 1, and 2. The bandwidth of the 900-nm absorption feature was found to grow with increasing barium concentration from 4.7 nm to a maximum of 15.9 nm. Emission spectra showed a similar bandwidth increase with barium content from 4.9 nm to a maximum of 10 nm. Emission cross sections for these materials were deduced by the methods of reciprocity, the Einstein method, and small-signal gain. The absorption feature's homogeneity was probed using a tunable pump source which qualitatively showed that the barium broadened lines were at least partly inhomogeneous. Each of these materials lased with a variety of output couplers. This family of materials was found to provide suitable laser hosts where a broader absorption and/or emission bandwidth is desired.
No takes yet. Share an insight, caveat, or question.
Bayramian et al. (1999) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: