Electrical, mechanical, and optical changes in MWCNT-doped PMMA composite films

In this study, we report the preparation of poly (methyl methacrylate)/multi-walled carbon nanotube (MWCNT) composite thin films by simple and efficient solution mixing and ultrasonic method and the electrical, optical, and mechanical characterizations. Scattered light intensity ( I sc ), tensile modulus ( E), and surface conductivity ( σ) of these composites have increased with the addition of MWCNT into the composite. The observed behavior in electrical, optical, and mechanical properties of the poly (methyl methacrylate)/MWCNT composites was interpreted by site and classical percolation theory. The optical mechanical and electrical percolation thresholds of poly (methyl methacrylate)/MWCNT composites were determined as φ op = 3 wt%, φ m = 0 wt%, and φ σ = 5 wt%, respectively. The optical ( t op ), mechanical ( t m ), and electrical ( t σ ) critical exponents were calculated as 2.23, 0.43, and 0.11, respectively. Both the tensile modulus and tensile strength of poly (methyl methacrylate)/MWCNT composites were increased with increasing MWCNT content until it reaches to 10 wt%. However, above φ = 10 wt%, the mechanical properties of the composites were decreased due to the aggregation of MWCNTs, while the toughness does not show a significant change until φ = 10 wt% MWCNT content, whereas it was decreased above this value.