The Effects of Partial Replacement of Ground Granulated Blast Furnace Slag by Ground Wood Ash on Alkali-Activated Binder Systems

Cement production contributes significantly to carbon dioxide emissions. Alkali-activated materials offer an environmentally friendly alternative due to their comparable strength, durability and low-carbon emissions while utilizing wastes and industrial by-products. Wood ash is a waste material that shows promising results as a partial replacement for Portland cement and precursors in alkali-activated systems. The aim of this study was to examine the effect of ground wood ash on the mechanical properties of alkali-activated mortars. Wood ash was incorporated as a 0 wt%, 10 wt% and 20 wt% partial replacement for ground granulated blast furnace slag (GGBFS). The wood ashes were ground in a planetary ball mill for 10 and 20 min. Sodium silicate (Na2SiO3), sodium carbonate (Na2CO3), and sodium hydroxide (NaOH) were used as alkali activators. The results demonstrated that ground wood ash improved the mechanical properties of alkali-activated systems compared to untreated wood ash. However, the incorporation of wood ash increased the porosity of the binder matrix.