Probing the Surface Chemistry of Lithium Nitridation

High Resolution Image Download MS PowerPoint Slide Chemical synthesis of Li 3 N through lithium nitridation has potential to advance rechargeable battery and nitrogen fixation technology. However, studies of the conditions for forming Li 3 N on the lithium surface via nitrogen gas exposure report contradictory findings, such as the spontaneous reaction of Li with pure N 2, the impossibility of forming Li 3 N through pure Li and N 2 interaction, the requirement of trace H 2 O to catalyze the reaction, and evidence to the contrary. In this study, ambient pressure X-ray photoelectron spectroscopy (APXPS) was applied to evaluate the in situ chemical evolution of the lithium metal surface under nitrogen gas up to 800 mTorr. At pressures ≤10 mTorr, no Li 3 N was detected. At higher pressures, surface Li 3 N rapidly reacts with trace CO 2 . Additionally, because metallic lithium is readily oxidized by trace gases, the atomic nitrogen concentration of the lithium surface remains below 2%. When nitridation follows oxidation by O 2 gas, CO 2 gas, or H 2 O vapor, surface Li 3 N formation is inhibited. These results suggest that nitrogen gas can diffuse through the oxidized lithium metal surface to react with subsurface metallic lithium.