Influence of Accelerated Weathering on the Properties of Polypropylene/Polylactic Acid/Eucalyptus Wood Composites

In the view of producing environmentally friendly materials without compromising properties, new composites containing polypropylene as a matrix and eucalyptus wood, with or without 15% of polylactic acid, were melt processed. In order to improve compatibility between components, a chemical modification of wood with toluene-2,4-diisocyanate (TDI) was realized and evidenced by changes in FT-IR and XPS spectra. The morphological, mechanical, and thermal characterizations of the obtained composites were evaluated before and after accelerating weathering. The results showed that the material comprising 15% TDI-modified wood, PP, and 15% PLA exhibited the best properties.