Understanding the mechanism of aluminium nanoparticle oxidation

Aluminium nanoparticles have gained importance in the last decade because of their increased reactivity as compared with traditional micron-sized particle. The physics of burning of aluminium nanoparticle is expected to be different than that of micron-sized particles, and the current article is motivated by these differences. We have previously measured the size resolved reactivity of nanoaluminium by single-particle mass spectrometry, to which we now add transmission electron microscope (TEM) and an on-line density measurement. The latter two studies revealed the presence of hollow particles following oxidation of nanoaluminium and indicating the significance of diffusion of aluminium in the overall process. Based on experimental evidence, we believe that aluminium nanoparticle oxidation occurs in two regimes. Prior to melting of aluminium slow oxidation occurs through the diffusion of oxygen through the aluminium oxide shell. Above the melting point, we transition to a fast oxidation regime whereby both aluminium and oxygen diffuse through the oxide shell to enhance the oxidation rate. We also develop a phenomenological model for nanoaluminium oxidation that accounts for the experimentally observed rates, the fact that both fuel and oxidizer are diffusing, and a new effect related to internal pressure gradients. The latter phenomen is based on molecular dynamic simulations suggesting that there are large pressure gradients present inside these particles, with the aluminium core under a positive pressure and the aluminium oxide shell under a negative pressure. We have considered the effect of these pressure gradients on the oxidation process. A power law relation was obtained (t ∝ r 1.6± 0.1) between the time required for oxidation and particle radius.