Critical Thickness of SiO₂ Coating Layer on Core@Shell Bulk@Nanowire Si Anode Materials for Li‐Ion Batteries

This is the authors' abstract. We don't add key points for this paper.

Amorphous SiO2 coating layers with thicknesses of ca. 2, 7, 10, and 15 nm are introduced into bulk@nanowire core@shell Si particles via direct thermal oxidation at 650-850 °C. Of the coated samples, Si with a coating thickness of ca. 7 nm has the best electrochemical performance. This sample shows an initial discharge capacity of 2279 mA h g(-1) with a Coulombic efficiency of 92% and displays 83% capacity retention after 50 cycles at 0.2C rate.