Reverse atom transfer radical solution polymerization of methyl methacrylate under pulsed microwave irradiation

The reverse atom transfer radical polymerization (RATRP) of methyl methacrylate (MMA) was successfully carried out under pulsed microwave irradiation (PMI) at 69 °C with N,N ‐dimethylformamide as a solvent and with azobisisobutyronitrile (AIBN)/CuBr 2 /tetramethylethylenediamine as an initiation system. PMI resulted in a significant increase in the polymerization rate of RATRP. A 10.5% conversion for a polymer with a number‐average molecular weight of 34,500 and a polydispersity index of 1.23 was obtained under PMI with a mean power of 4.5 W in only 52 min, but 103 min was needed under a conventional heating process (CH) to reach a 8.3% conversion under identical conditions. At different [MMA] 0 /[AIBN] 0 molar ratios, the apparent rate constant of polymerization under PMI was 1.5–2.3 times larger than that under CH.