A Large Thermal Hysteresis Loop Produced by a Charge-Transfer Phase Transition in a Rubidium Manganese Hexacyanoferrate

In a rubidium manganese hexacyanoferrate, RbMn[Fe(CN)(6)], the magnetic susceptibility (chi(M)) decreased at 225 K (=T(1/2)decreasing) and abruptly increased at 300 K (=T(1/2)increasing) in the cooling and warming processes, respectively. X-ray photoelectron spectroscopy and infrared spectroscopy indicated that the high-temperature (HT) and low-temperature (LT) phases were composed of Mn(II)-NC-Fe(III) and Mn(III)-NC-Fe(II), respectively. A structural change from cubic (F43m, a = 10.533 A) to tetragonal (I4m2, a = b = 7.090 A, c = 10.520 A) accompanied the phase transition, and, on the basis of these results, the HT and LT phases were assigned to Mn(II)(t(2g)(3)e(g)(2), (6)A(1g); S = (5)/(2))-NC-Fe(III) (t(2g)(5), (2)T(2g); S = (1)/(2)) and Mn(III)(e(g)(2)b(2g)(1)a(1g)(1), (5)B(1g); S = 2)-NC-Fe(II) (b(2g)(2)e(g)(4), (1)A(1g); S = 0), respectively. This phenomenon is caused by a metal-to-metal charge transfer from Mn(II) to Fe(III) and a Jahn-Teller distortion of the produced Mn(III) ion. The reaction mechanism is discussed, considering the entropy difference between the HT and LT phases.