Solution-Processed BiI₃ Thin Films for Photovoltaic Applications: Improved Carrier Collection via Solvent Annealing

We report all-inorganic solar cells based on solution-processed BiI 3 . Two-electron donor solvents such as tetrahydrofuran and dimethylformamide were found to form adducts with BiI 3, which make them highly soluble in these solvents. BiI 3 thin films were deposited by spin-coating. Solvent annealing BiI 3 thin films at relatively low temperatures (≤100 °C) resulted in increased grain size and crystallographic reorientation of grains within the films. The BiI 3 films were stable against oxidation for several months and could withstand several hours of annealing in air at temperatures below 150 °C without degradation. Surface oxidation was found to improve photovoltaic device performance due to the formation of a BiOI layer at the BiI 3 surface which facilitated hole extraction. Nonoptimized BiI 3 solar cells achieved the highest power conversion efficiencies of 1.0%, demonstrating the potential of BiI 3 as a nontoxic, air-stable metal-halide absorber material for photovoltaic applications.