High burnup MOX and UO2 test rods were prepared from the fuel rods irradiated in commercial BWRs. Each test rod was equipped with a fuel center thermocouple and reirradiated in the Halden boiling water reactor (HBWR) in Norway. The burnups of MOX and UO2 test rods reached about 84GWd/tHM and 72GWd/t, respectively. Fuel temperature was measured continuously during the re-irradiation tests. Thermal conductivity change in high burnup fuel was evaluated from the results of comparison between the measured fuel temperature and the data calculated by using the fuel analysis code FEMAXI-6. The comparison results suggested that the thermal conductivity of MOX fuel pellets is comparable to that of UO2 fuel pellets in the high burnup region around 80 GWd/t. It is probable that the impurity effect of Pu atoms gradually diminishes with increasing burnup because other factors that affect pellet thermal conductivity, such as the accumulation effect of soluble fission products and irradiation-induced defects in crystal lattice, become dominant in a high burnup region.