High‐Pressure Synthesis of Manganese Oxyhydride with Partial Anion Order

The high-pressure synthesis of a manganese oxyhydride LaSrMnO3.3 H0.7 is reported. Neutron and X-ray Rietveld analyses showed that this compound adopts the K2 NiF4 structure with hydride ions positioned exclusively at the equatorial site. This result makes a striking contrast to topochemical reductions of LaSrMnO4 that result in only oxygen-deficient phases down to LaSrMnO3.5 . This suggests that high H2 pressure plays a key role in stabilizing the oxyhydride phase, offering an opportunity to synthesize other transition-metal oxyhydrides. Magnetic susceptibility revealed a spin-glass transition at 24 K that is due to competing ferromagnetic (Mn(2+) -Mn(3+) ) and antiferromagnetic (Mn(2+) -Mn(2) , Mn(3+) -Mn(3+) ) interactions.