Electrically Conductive PEDOT Coating with Self-Healing Superhydrophobicity

A self-healing electrically conductive superhydrophobic poly(3,4-ethylenedioxythiophene) (PEDOT) coating has been prepared by chemical vapor deposition of a fluoroalkylsilane (POTS) onto a PEDOT film, which was obtained by electrochemical deposition. The coating not only maintained high conductivity with a low resistivity of 3.2 × 10(-4) Ω·m, but also displayed a water contact angle larger than 156° and a sliding angle smaller than 10°. After being etched with O2 plasma, the coating showed an excellent self-healing ability, spontaneously regaining its superhydrophobicity when left under ambient conditions for 20 h. This superhydrophobicity recovery process was found to be humidity-dependent, and could be accelerated and completed within 2 h under a high humidity of 84%. The coating also exhibited good superhydrophobicity recovering ability after being corroded by strong acid solution at pH 1 or strong base solution at pH 14 for 3 h.