Fuel Cell Membranes Based on Grafted and Post‐Sulfonated Glycidyl Methacrylate (GMA)

Glycidyl methacrylate (GMA) was pre‐irradiation grafted into ETFE base film of 25 μm thickness up to graft levels of 300%. The grafted films were sulfonated using a mixture of sulfite and bisulfite. FTIR and SEM–EDX analysis of the synthesized films and membranes was performed to confirm the grafting and the sulfonation. A pronounced front mechanism for grafting of GMA into ETFE was found. Regarding ex situ fuel cell relevant properties, conductivities of up to 0.25 S cm –1 were attained. For the first time, fuel cell testing of this type of membrane is reported. These grafted membranes performed comparable to a commercial benchmark membrane (Nafion® 212) and better than a styrene‐based grafted membrane with similar conductivity. Post‐test FTIR analysis showed that a fraction of the grafted chains was lost during the test under constant current conditions, yet the membrane still exhibited superior durability compared to a styrene‐based grafted membrane. Hydrolysis of the methacrylate groups was shown not to be the principle cause of the loss of sulfonic acid groups.