Layered perovskites as promising cathodes for intermediate temperature solid oxide fuel cells

The suitability of GdBaCo2O5+δ as a cathode material for intermediate temperature solid oxide fuel cells has been evaluated. The 18O/16O isotope exchange depth profile (IEDP) method has been used to obtain the oxygen surface exchange and oxygen tracer diffusion coefficients yielding optimum values for applicability in fuel cells (k* = 2.8 × 10−7 cm s−1 and D* = 4.8 × 10−10 cm2 s−1 at 575 °C) especially in terms of low activation energies (EAk = 0.81(4) and EAD = 0.60(4) eV). The same material has been characterized electrically as a part of a symmetrical electrochemical system (GdBaCo2O5+δ/Ce0.9Gd0.1O2−x/GdBaCo2O5+δ), by means of impedance spectroscopy measurements, corroborating an excellent performance in the classical intermediate temperature range for solid oxide fuel cells (500–700 °C). An area specific resistance (electrode–electrolyte interface) of 0.25 Ω cm2 at 625 °C was achieved for a cell processing temperature of 975 °C. Finally, layered perovskites are presented as a promising new family of materials for cathode use in solid oxide fuel cells at low temperatures.