Sol–Gel Synthesis of Mesoporous Silica–Iron Composite: Kinetics, Equilibrium and Thermodynamics Studies for the Adsorption of Turquoise-Blue X-GB Dye

Mesoporous silica (MPS) and MPS-Fe composite was prepared via sol–gel technique and characterized by BET, FTIR, XRD, SEM and pZc. The MPS and MPS-Fe adsorption efficiencies were evaluated for a cationic dye Turquoise-blue X-GB. The MPS-Fe composite showed pore size and BET values of 9.52 nm and 309 m 2 /g, respectively. XRD and SEM analysis revealed the amorphous nature and uniform distribution of spherical partciles with average particle size of 50 nm of MPS-Fe composite. The points of zero (pZc) charge found to be 2.3 and 6.3 for MPS and MPS-Fe, respectively. The MPS and MPS-Fe showed promising efficiency for the adsorption of Turquoise-blue X-GB as a function of medium pH, contact time, dye initial concentration and temperature. Among, Freundlich, Langmuir, Harkins–Jura, Temkin, Doubinin–Radushkevich isotherms, the Turquoise-blue X-GB followed Langmuir isothermal model with adsorption capacities of 83.34 mg/g and 74.07 mg/g for MPS and MPS-Fe composite, respectively. Among kinetics models, pseudo second order kinetic model fitted to the dye adsorption with R 2 values of 0.998 and 0.988 for MPS and MPS-Fe composite, respectively. The negative values of enthalpy (ΔH) and free energy (ΔG) revealed exothermic and spontaneous adsorption of dye at room temperature. Results revealed that MPS and MPS-Fe composite have promising potential for Turquoise-blue X-GB dye adsorption and could possibly be extended for the adsorption of dyes from textile effluents.