Polyester from dimethylketene and acetaldehyde: Direct copolymerization and β‐lactone ring‐opening polymerization

Two ways to obtain aliphatic polyesters (PEs) from dimethylketene and acetaldehyde were investigated. On the one hand, a direct anionic copolymerization was carried out in toluene at −60 °C. The resulting polymer was mainly composed of PE units. On the other hand, a two‐step process involving the synthesis of 3,3,4‐trimethyl‐2‐oxetanone by [2+2] cycloaddition, followed by its ring‐opening polymerization, with various initiators and solvents, led to the expected PE. Molecular weights up to 9000 g mol −1 (measured by nuclear magnetic resonance (NMR)), with narrow polydispersity around 1.2, were obtained. These polymers were found stable up to 274 °C under nitrogen and a broad and complex endothermic peak attributed to crystallinity was observed near 139 °C by differential scanning calorimetry (DSC). The crystallinity, measured by X‐ray diffraction, was close to 0.45.