Rate dependent structural changes, cycling stability, and Li-ion diffusivity in a layered–layered oxide cathode material after prolonged cycling

This work shows that cycling at a high rate can reduce the structural transition of a layered–layered oxide cathode material during cycling, resulting in a higher cycling stability and faster Li ion diffusion at prolonged cycles.