Influence of interchain forces and supermolecular structure on the drawing behavior of nylon 66 fibers in the presence of supercritical carbon dioxide

The drawing behavior and mechanical properties of as‐spun and highly oriented nylon 66 fibers drawn in supercritical carbon dioxide (SCCO 2 ) were investigated. Conditions including different temperatures, CO 2 pressures, and plasticizers with different polarity were systematically studied. Results indicate that CO 2 is an efficient plasticizer for as‐spun nylon 66 fibers as shown by decreases in the draw stress. In contrast, CO 2 shows only a slight influence on the drawability of highly oriented nylon 66 fiber. The effect of other plasticizers such as water, methanol, and ethanol on the drawability of nylon 66 fibers is very similar to that of CO 2 . Tenacity and modulus of one‐stage drawn fibers were less than 0.8 and 5.0 GPa, respectively. Fibers with the highest tenacity and modulus, 0.96/5.04 and 1.06/5.04 GPa, were obtained by two‐stage drawing in SCCO 2 from as‐spun and drawn nylon 66 fibers, respectively. The main reason for the extremely low draw ratios (<6.0) of nylon 66 fibers was the presence of hydrogen bonds in the crystalline phase.