Enhanced Breakdown Voltage With High Johnson's Figure-of-Merit in 0.3-μ m T-gate AlGaN/GaN HEMTs on Silicon by ( NH₄)₂ Sₓ Treatment

Enhanced OFF -state breakdown voltage has been observed in ammonium sulfide [(NH4)2Sx]-treated AlGaN/GaN high electron mobility transistors (HEMTs) on Si substrate without compromising the unit gain cutoff frequencies. About six times higher OFF -state breakdown voltage (BVgd) and three orders of magnitude higher ION/IOFFratio were observed in the (NH4)2Sx-treated 0.3- μm T-gate conventional AlGaN/GaN HEMTs on Si substrate. In addition, three orders of magnitude lower surface leakage current (~3.0 μA/mm to ~3 nA/mm) have also been observed on the (NH4)2Sx-treated devices. The calculated Johnson's figures of merit (J-FOM = BVgd× fT) is 5.41 × 1012V/s, which is the highest value reported so far for 0.3- μm T-gate conventional SiN passivated AlGaN/GaN HEMTs without the incorporation of field plate. No significant drain current collapse was observed on the (NH4)2Sx-treated devices.