Design of novel RGO/2D strip-like ZIF-8/DMAOP ternary hybrid structure towards high-efficiency microwave absorption, active and passive anti-corrosion, and synergistic antibacterial performance

This is the authors' abstract. We don't add key points for this paper.

In order to meet the requirements of the marine environment for microwave absorption (MA) materials, we put forward the strategy of constructing multi-functional composite materials, which integrate microwave absorption, anti-corrosion, and antibacterial properties. Herein, graphene oxide (GO) was used as a template to induce the growth of zeolitic imidazolate framework-8 (ZIF-8), simultaneously as a two-dimensional (2D) nanocontainers to load corrosion inhibitors to achieve pH-responsive and self-healing properties. Finally, quaternary ammonium salt (dimethyl octadecyl(3-trimethoxylsilyl propyl) ammonium chloride (DMAOP)) and sodium ascorbate (VCNa) were introduced to achieve synergistic antibacterial activity and the reduction of GO. The 2D strip-like structure of ZIF-8 was due to the confined growth induced by the electrostatic attraction between ZIF-8 and GO sheets. The as-obtained reduced GO (RGO)/ZIF-8/DMAOP 5 exhibited excellent microwave absorption (MA) properties, with a minimum reflection loss (RL) value of −47.08 dB at 12.73 GHz when the thickness was 2.8 mm. Moreover, the effective absorption bandwidth reached 6.84 GHz. After soaking in 3.5% NaCl solution for 35 days, the RGO/ZIF-8/DMAOP 5 −0.7% coating still achieved an impedance value of 4.585 × 10 7 Ω·cm 2 and a protective efficiency of 99.994%, providing superior anti-corrosion properties. In addition, fantastic antibacterial activity was obtained, with the antibacterial rates of RGO/ZIF-8/DMAOP 10 reaching 99.39% and 100% against Escherichia coli and Staphylococcus aureus . This work could open new avenues towards the development of a new generation of multifunctional MA materials.