Fabrication of Mesoporous SiO₂ Shells for Dye Adsorption Studies

The present work focuses on the fabrication of novel hybrid materials for toxic dye removal from an aqueous environment. Nanocarbon template (20-30 nm) was coated with tri-ethyl-orthosilicate (TEOS). The core-shell structure developed was further air pyrolyzed at 600 °C to produce mesoporous silica shells. The pore structures and characteristics of the material were evaluated using XRD, nitrogen adsorption studies, SEM, and TEM. Owing to the hierarchical porosity in range of 1-4 nm and 10-20 nm their adsorption studies were investigated for Phenol-Red. Dye adsorption studies performed revealed 98% removal efficiency with only 20 mg of adsorbent dose within 15 minutes.