The variation of the enhanced photoluminescence efficiency of Y_2O_3:Eu^3+films with the thickness to the photonic crystal layer

This study examined the effects of the thickness of Y(2)O(3):Eu(3+) phosphor films on quartz substrates coated with two-dimensional (2D) SiO(2) square-lattice nanorod photonic crystal layers (PCL) at identical heights on their extraction and absorption efficiency. The photoluminescence (PL) efficiency enhancement ratio decreased exponentially with increasing Y(2)O(3):Eu(3+) film thickness. The 2D PCL-assisted Y(2)O(3):Eu(3+) film with a thickness (t) = 400 nm showed enhancement in the upward and downward PL emission by factors of 6.2 and 8.6, respectively, with respect to those of a conventional flat film. This observation was attributed to diffraction scattering of the excitation and emission light.