Exploring strain rate effects upon 3D materials using high speed in situ X-ray tomoscopy

Cellular materials are ubiquitous in our modern society. They may be stochastic gas-blown foams (e.g., polyurethane), foamed starches (e.g., cereals), or, in this case, 3D printed microlattices. Failure in these materials is often driven by surface or sub-surface defects, which may be nucleated at a surface roughness, an interior void, or inclusion interfaces that may not be typically observable . Obfuscating our understanding further, bulk materials are known to exhibit strain-rate-dependent mechanical response, making a subsurface understanding of damage even more critical. For the first time, an in situ uniaxial mechanical loading stage that simultaneously rotates specimens up to 18 Hz was fielded at a synchrotron for 3D tomographic imaging. This capability opens a plethora of materials science opportunities to explore strain rate effects in materials and examining deformation, fracture, and delamination’s (in composites) for a complete 3D picture (movie) of material response. We demonstrate the deformation of 3D printed polymer lattice structures, of three different material types, at 0.25, 1.1, and 2.2 s −1 strain rates. We successfully imaged the 3D deformation of these materials and can directly compare the same printed structure to the three material types at three strain rates, all in 3D. Material point method simulations were applied to one of the materials to better understand the role of voids on the 3D printed structure’s performance. • In situ synchrotron X-ray tomographic imaging of lattice materials during simultaneous uniaxial loading. • Strain rates between 0.25 and 2.2 /s were explored during 3D imaging. • 3D printed structures provide replicates to material and explore strain rate effects. • Dual Domain Material Point Modeling method is used to explore large deformations of lattice structures.