SmCo/Cr thin films with coercivity up to 3000 Oe were prepared by RF-diode sputtering. Hard disks were fabricated using glass substrates and the recording properties, carrier-to-integrated-noise ratio, media noise, and overwritability were evaluated using conventional thin-film inductive heads. The influence of the thickness of the Cr underlayer, SmCo magnetic layer, and Cr overlayer on media noise was studied. The intergranular exchange and magnetostatic interaction effects present in SmCo/Cr media were measured from their remanence magnetization curves and correlated with media noise values obtained from recording measurements. The media noise in SmCo/Cr disks varied little with increasing linear density, and no supralinear increase in noise as explained by a transition noise model was observed. A thin Cr underlayer (>