Lubrication-Enhanced Mechanisms of Bentonite Grease Using 2D MoS2 with Narrow Lateral Size and Thickness Distributions

2D MoS2 with narrow lateral size and thickness distributions was introduced to promote the anti-friction and anti-wear properties of the bentonite grease (BG) in a state of boundary lubrication. Optical microscopy (OM), and 3D optical profilers (3D OP), Raman spectrometry (Raman), scanning electron microscope, energy dispersion spectrum (SEM-EDS), and X-ray photoelectron spectroscopy (XPS) were applied to characterize the wear surface of the GCr15 bearing steel/GCr15 bearing steel contact. It is found that the average friction coefficient (AFC), wear scar diameter (WSD), surface roughness and average wear scar depth of BG + 1.2 wt.% 2D MoS2 were effectively reduced by approximately 22.15%, 23.14%, 55.15%, and 21.1%, respectilvely, compared with BG under the working condition of 392N, 75 °C, 1 h, and 1200 rpm. Raman, EDS and XPS results jointly demonstrated that a stable adsorbed film and a robust tribochemical film composed of Fe2O3, FeSO4, Fe2(SO4)3, FeSO3, FeS, FeO and MoO3, which further contributes to the enhancement of lubrication performance.