We have studied the degradation of MgB/sub 2/ thin films, grown by hybrid physical-chemical vapor deposition (HPCVD), by submerging MgB/sub 2/ films into de-ionized water at different temperatures. The thickness, room temperature resistance, and superconducting transition were measured as a function of time in water and the temperature of the water. Results show that the films degrade faster at room temperature than at 0/spl deg/C. The room temperature resistance increases with time. The thickness of the MgB/sub 2/ films decreases rapidly initially, but then saturates. The resultant material is amorphous and insulating. Both T/sub c/(onset) and T/sub c/(0) of the MgB/sub 2/ films decrease with time in water, while the superconducting transition become broader. The effects of the exposure to other solvents and photoresist were also studied, and it was found that isopropanol does not cause MgB/sub 2/ films to degrade.
No takes yet. Share an insight, caveat, or question.
Cui et al. (2005) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: