Anionic ring‐opening polymerization of propylene oxide in the presence of phosphonium catalysts

Anionic ring‐opening polymerization of propylene oxide in the presence of potassium alcoholate initiator was accelerated by addition of the bulky phosphonium salt tetrakis[cyclohexyl(methyl)amino]phosphonium‐tetrafluoroborate. Dipropylene glycol (DPG) was partially deprotonated (5%) and used as an initiator for the polymerization performed at 100 °C at normal pressure. The delocalization of the positive charge over five atoms promoted the formation of a separated ion pair, thus enhancing nucleophilicity and reactivity. Compared with those of polyaminophosphazenes and tetrabutylphosphonium cation, the average propagation rates increased in the order of Bu 4 P + , K + , P , P , and t BuP 4 H + . DP n for the polymers was in the range of 20–64. Characterization of poly(propylene oxide)s by means of 1 H NMR, size exclusion chromatography (SEC), and matrix‐assisted laser desorption/ionization time‐of‐flight mass spectrometry (MALDI‐TOF‐MS) showed low polydispersities ( M w / M n ) without any byproducts or impurities. The M w / M n obtained was 1.03–1.09 (MALDI‐TOF‐MS) and 1.11–1.15 (SEC), respectively. Values calculated from titration of the hydroxyl groups showed good agreement. Determination of the total degree of unsaturation in the range of 13–60 mmol/kg indicated larger amounts with increasing polymerization rates.