Composting Short Paper Fiber with Broiler Litter and Additives: Part I: Effects of Initial pH and Carbon/Nitrogen Ratio On Ammonia Emission

Short paper fiber (SPF), a by-product of the paper mill industry, was cocomposted with broiler litter (BL) to determine decomposition rate and NH3-N loss as functions of C/N ratio and pH of the compost mixes. The SPF generally had a high C/N ratio >200 while the BL, consisting of bedding material (sawdust) and poultry manure, had a low C/N ratio of 10–12. A total of seven series (27 tests) of pilot-scale studies were conducted using two different SPFs mixed with BL. Additives used for pH control were alum (aluminum sulfate), HiClay® Alumina and sulfuric acid. Mixing ratios [SPF/(SPF+BL), kg/kg(dry basis)] used were 0.8 to 0.4. Test conditions were C/N of 17 to 49, pH of 6.6 to 8.3, initial temperatures of −1 to 22°C, composting temperature of 60°C, water content of 50-55% w.b. and remixing two times per week. Composting temperature was controlled using forced ventilation with a high/low fan setting. Composting trials lasted two weeks. Ammonia loss, O2, CO2, compost temperatures and dry solids loss were measured. Evaluations of ammonia emissions versus initial C/N and pH showed: (1) NH3-N loss decreased as initial C/N increased, even above C/N = 38; (2) NH3-N loss decreased rapidly below pH = 7 and increased rapidly for initial pH above 8. Addition of alum and/or sulfuric acid was found to decrease NH3- N loss while HiClay® Alumina had little or no effect. Results on dry solids loss are not presented in this article.