Alternating current losses in YBa2Cu3O7−x coated conductors on technical substrates

We report on measurements of the ac losses of YBa2Cu3O7−x conductors on technical substrates. The samples are taken from conductors 1 m long produced with an ion beam assisted deposition step in the manufacturing process yielding 1 cm wide conductors with critical currents approaching 100 A at 77.4 K. The losses due to combinations of ac transport currents and ac magnetic fields were measured calorimetrically and the results compared to theoretical estimates. While the results of our measurements are similar to the theoretical estimates, there are some important differences in the qualitative behavior.