Synthesis of thermoplastic polyurethane and its physical and shape memory properties

In this article, thermoplastic polyurethane (PU) with a shape memory property was synthesized. First, the PU prepolymer was prepared by reacting poly(tetramethylene glycol) with 4,4′‐diphenylmethane diisocyanate, then extended with various extenders such as linear aliphatic 1,4‐butanediol, benzoyl‐type 4,4‐bis(4‐hydroxyhexoxy)‐isopropylane and naphthalate‐type bis(2‐phenoxyethanol)‐sulfone or naphthoxy diethanol. The experimental results showed that the tensile strength, elongation at break, and initial modulus at 300% of these copolymer films were in the range of 31–64 Mpa, 42%–614%, and 8.26–11.5 MPa, respectively. Thermal analysis showed that the glass‐transition temperature of these copolymers was in the range of −73°C to −50°C for the soft segment ( T g s ) and 70°C–106°C for the hard segment ( T g h ) and that the melting point was in the range of 14.6°C–24.2°C for the soft segment and 198°C–206°C for the hard segment. The extender with a benzoyl or naphthalate group was better able to promote its shape memory property than was the regular polyurethane.