Pulsed Electric Current Sintering of Silicon Nitride

Pulsed electric current sintering (PECS) has been used to densify α‐Si 3 N 4 powder doped with oxide additives of Y 2 O 3 and Al 2 O 3 . A full density (>99%) was achieved with virtually no transformation to β‐phase, resulting in a microstructure with fine equiaxed grains. With further holding at the sintering temperature, the α‐to‐β phase transformation took place, concurrent with an exaggerated grain growth of a limited number of elongated β‐grains in a fine‐grained matrix, leading to a distinct bimodal grain size distribution. The average grain size was found to obey a cubic growth law, indicating that the growth is diffusion‐controlled. In contrast, the densification by hot pressing was accompanied by a significant degree of the phase transformation, and the subsequent grain growth gave a broad normal size distribution. The apparent activation energy for the phase transformation was as high as 1000 kJ/mol for PECS, almost twice the value for hot pressing (∼500 kJ/mol), thereby causing the retention of α‐phase during the densification by PECS.