Embrittlement of titanium–zirconium ‘null-matrix’ alloy by deuterium

Random substitutional Ti 2.08 Zr exhibits zero Bragg scattering and alloys with this nominal composition are therefore used to fabricate pressure cells for neutron scattering measurements. Because Ti and Zr alloys are well known to be subject to hydrogen embrittlement, the embrittlement of Ti 2.001 Zr by deuterium gas was investigated to assess its suitability for use in neutron diffraction experiments on samples under deuterium pressure. At 77°C, the alloy survived 15 days in 689 bar D 2 with no apparent effect on mechanical properties. At 100°C, however, embrittlement was initiated by 607-bar D 2 , and at 200°C rapid decrepitation occurred, producing ε-(TiZr)D x . It is therefore recommended that Ti ≈2 Zr should not be considered for structural use with deuterium gas above room temperature.