Pristine point of zero charge (p.p.z.c.) and zeta potentials of boehmite’s nanolayer and nanofiber surfaces

The pristine point of zero charge (p.p.z.c) and zeta potential as a function of pH of boehmite oxide/hydroxide (α-Al2O3·H2O) have been determined for three filter media. The active component in the first two filter media is boehmite nanofibers, only 2 nm in diameter and about 300 nm long. Boehmite nanofibers create high zeta potential (ζtrue≥46 mV) in aqueous solutions in the pH range of 3–8. The p.p.z.c. values were determined to be 11.60 ± 0.15 for nanofibers grafted onto microglass fibers and 11.40 ± 0.15 for agglomerated nanofibers. In the third filter media, a boehmite nanolayer in the form of monocrystalline oxide/hydroxide with a thickness of approximately 1.2 nm is electroadhesively deposited onto siliceous support material with large surface area of about 50 m2/g, therefore forming a highly electropositive composite of boehmite nanolayer on the second highly electronegative solid. Boehmite’s oxide-hydroxide nanolayer surface creates high zeta potential (ζtrue≥50 mV) in aqueous solutions in the pH range of 3–8. The p.p.z.c. value was determined to be 11.38 ± 0.15. The reported values are within accuracy, but they are much higher than the values reported in the literature. X-ray powder diffraction data were supplemented by microscopy, infrared spectroscopy in order to characterize fully synthetic boehmite surfaces.