Conductive Holey MoO₂–Mo₃N₂ Heterojunctions as Job-Synergistic Cathode Host with Low Surface Area for High-Loading Li–S Batteries

Li–S batteries have several advantages in terms of ultrahigh energy density and resource abundance. However, the insulating nature of S and Li 2 S, solubility and shuttle effects of lithium polysulfides (LiPSs), and slow interconversion between LiPSs and S/Li 2 S/Li 2 S 2 are significant impediments to the commercialization of Li–S batteries. Exploration of the advanced S host skeleton simultaneously with high conductivity, adsorbability, and catalytic activity is highly desired. Herein, a heterojunction material with holey nanobelt morphology and low surface area (95 m 2 /g) is proposed as a compact cathode host to enable a conformal deposition of S/Li 2 S with homogeneous spatial distribution. The rich heterointerfaces between MoO 2 and Mo 3 N 2 nanodomains serve as job-synergistic trapping-conversion sites for polysulfides by combining the merits of conductive Mo 3 N 2 and adsorptive MoO 2 . This non-carbon heterojunction substrate enables a high S loading of 75 wt % even under low surface area. The initial capacity of MoO 2 –Mo 3 N 2 @S reaches 1003 mAh/g with a small decay rate of 0.024% per cycle during 1000 cycles at 0.5 C. The long-term cyclability is preserved even under a high loading of 3.2 mg/cm 2 with a reversible capacity of 451 mAh/g after 1000 cycles. The Li-ion diffusion coefficient for MoO 2 –Mo 3 N 2 @S is extremely high (up to 2.7 × 10 –7 cm 2 /s) benefiting from LiPS conversion acceleration at heterojunctions. The affinity between LiPSs and heterojunction allows a dendrite-free Li plating at anode even after long-term cycling. Well-defined heterointerface design with job-sharing or job-synergic function appears to be a promising solution to high-performance Li–S batteries without the requirement of loose or high-surface-area carbon network structures.