White polymer light emitting diodes based on PVK: the effect of the electron injection barrier on transport properties, electroluminescence and controlling the electroplex formation

. The electron injection barrier is also found to play a major role in defining the EL spectra of the PLEDs. A larger injection barrier gives rise to electroplex formation in the EML-ETL interface of the PLEDs and an additional peak at ∼605 nm was observed in the EL spectrum. As a result, a near white emission with CIE coordinates of (0.30, 0.30) and (0.25, 0.23) at 20 V was obtained from devices with BCP and BPhen as ETLs. Furthermore, PVK doped with 2-phenyl-5-(4-biphenylyl)-1,3,4-oxadiazole (PBD) at 10, 20 and 30 wt% ratios modified the electron transport nature of PVK and had a remarkable influence on the aforesaid properties, especially on the electroplex formation.